奥氏体型耐热钢的化学成分(GB/T 4238—2007) |
|||||||||||||
|
GB/T 20878 中序号 |
新牌号 |
旧牌号 |
化学成分(质量分数)/% |
||||||||||
|
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
N |
V |
其他 |
|||
|
13 |
12Cr18Ni9 |
1Cr18Ni9 |
0.15 |
0.75 |
2.00 |
0.045 |
0.030 |
8.00~11.00 |
17.00~19.00 |
— |
0.10 |
— |
— |
|
14 |
12Cr18Ni9Si3 |
1Cr18Ni9Si3 |
0.15 |
2.00~3.00 |
2.00 |
0.045 |
0.030 |
8.00~10.00 |
17.00~19.00 |
— |
0.10 |
— |
— |
|
17 |
06Cr19Ni9① |
0Cr18Ni9 |
0.08 |
0.75 |
2.00 |
0.045 |
0.030 |
8.00~10.50 |
18.00~20.00 |
— |
0.10 |
— |
— |
|
19 |
07Cr19Ni10 |
— |
0.04~ 0.10 |
0.75 |
2.00 |
0.045 |
0.030 |
8.00~10.50 |
18.00~20.00 |
— |
— |
— |
— |
|
29 |
06Cr20Ni11 |
— |
0.08 |
0.75 |
2.00 |
0.045 |
0.030 |
10.00~12.00 |
19.00~21.00 |
— |
— |
— |
— |
|
31 |
16Cr23Ni13 |
2Cr23Ni13 |
0.20 |
0.75 |
2.00 |
0.045 |
0.030 |
12.00~15.00 |
22.00~24.00 |
— |
— |
— |
— |
|
32 |
06Cr23Ni13 |
0Cr23Ni13 |
0.08 |
0.75 |
2.00 |
0.045 |
0.030 |
12.00~15.00 |
22.00~24.00 |
— |
— |
— |
— |
|
34 |
20Cr25Ni20 |
2Cr25Ni20 |
0.25 |
1.50 |
2.00 |
0.045 |
0.030 |
19.00~22.00 |
24.00~26.00 |
— |
— |
— |
— |
|
35 |
06Cr25Ni20 |
0Cr25Ni20 |
0.08 |
1.50 |
2.00 |
0.045 |
0.030 |
19.00~22.00 |
24.00~26.00 |
— |
— |
— |
— |
|
38 |
06Cr17Ni12Mo2 |
0Cr17Ni12Mo2 |
0.08 |
0.75 |
2.00 |
0.045 |
0.030 |
10.00~14.00 |
16.00~18.00 |
2.00~3.00 |
0.10 |
— |
— |
|
49 |
06Cr19Ni13Mo3 |
0Cr19Ni13Mo3 |
0.08 |
0.75 |
2.00 |
0.045 |
0.030 |
11.00~15.00 |
18.00~20.00 |
3.00~4.00 |
0.10 |
— |
— |
|
55 |
06Cr18Ni11Ti |
0Cr18Ni10Ti |
0.08 |
0.75 |
2.00 |
0.045 |
0.030 |
9.00~12.00 |
17.00~19.00 |
— |
— |
— |
Ti≥5C |
|
60 |
12Cr16Ni35 |
1Cr16Ni35 |
0.15 |
1.50 |
2.00 |
0.030 |
0.005 |
33.00~37.00 |
14.00~17.00 |
— |
— |
— |
— |
|
62 |
06Cr18Ni11Nb① |
0Cr18Ni11Nb |
0.08 |
0.75 |
2.00 |
0.045 |
0.030 |
9.00~13.00 |
17.00~19.00 |
— |
— |
— |
Nb:10×C~0.10 |
|
66 |
16Cr25Ni20Si2 |
1Cr25Ni20Si2 |
0.20 |
1.50~2.50 |
1.50 |
0.045 |
0.30 |
18.00~21.00 |
24.00~27.00 |
— |
— |
— |
— |
|
注：表中所列成分除标明范围或最小值，其余均为最大值。 ① 为相对于GB/T 20878调整化学成分的牌号。 |
|||||||||||||