一般用途耐热钢和合金铸件室温力学性能与最高使用温度 |
|||||
|
牌 号 |
σp0.2/MPa |
σb/MPa |
δ/% |
HBS |
最高使用温度①/℃ |
|
(最小值) |
(最小值) |
(最小值) |
|||
|
ZG30Cr7Si2 |
— |
— |
— |
— |
750 |
|
ZG40Cr13Si2 |
— |
— |
— |
300② |
850 |
|
ZG40Cr17Si2 |
— |
— |
— |
300② |
900 |
|
ZG40Cr24Si2 |
— |
— |
— |
300② |
1050 |
|
ZG40Cr28Si2 |
— |
— |
— |
320② |
1100 |
|
ZGCr29Si2 |
— |
— |
— |
400② |
1100 |
|
ZG25Cr18Ni9Si2 |
230 |
450 |
15 |
— |
900 |
|
ZG25Cr20Ni14Si2 |
230 |
450 |
10 |
— |
900 |
|
ZG40Cr22Ni10Si2 |
230 |
450 |
8 |
— |
950 |
|
ZG40Cr24Ni24Si2Nb1 |
220 |
400 |
4 |
— |
1050 |
|
ZG40Cr25Ni12Si2 |
220 |
450 |
6 |
— |
1050 |
|
ZG40Cr25Ni20Si2 |
220 |
450 |
6 |
— |
1100 |
|
ZG45Cr27Ni4Si2 |
250 |
400 |
3 |
400③ |
1100 |
|
ZG40Cr20Co20Ni20Mo3W3 |
320 |
400 |
6 |
— |
1150 |
|
ZG10Ni31Cr20Nb1 |
170 |
440 |
20 |
— |
1000 |
|
ZG40Ni35Cr17Si2 |
220 |
420 |
6 |
— |
980 |
|
ZG40Ni35Cr26Si2 |
220 |
440 |
6 |
— |
1050 |
|
ZG40Ni35Cr26Si2Nb1 |
220 |
440 |
4 |
— |
1050 |
|
ZG40Ni38Cr19Si2 |
220 |
420 |
6 |
— |
1050 |
|
ZG40Ni38Cr19Si2Nb1 |
220 |
420 |
4 |
— |
1100 |
|
ZNiCr28Fe17W5Si2C0.4 |
220 |
400 |
3 |
— |
1200 |
|
ZNiCr50Nb1C0.1 |
230 |
540 |
8 |
— |
1050 |
|
ZNiCr19Fe18Si1C0.5 |
220 |
440 |
5 |
— |
1100 |
|
ZNiFe18Cr15Si1C0.5 |
200 |
400 |
3 |
— |
1100 |
|
ZNiCr25Fe20Co15W5Si1C0.46 |
270 |
480 |
5 |
— |
1200 |
|
ZCoCr28Fe18C0.3 |
④ |
④ |
④ |
④ |
1200 |
|
①最高使用温度取决于实际使用条件，所列数据仅供用户参考。这些数据适用于氧化气氛，实际的合金成分对其也有影响。 ②退火态最大HBS值，铸件也可以铸态提供，此时硬度限制不适用。 ③最大HBS值。 ④由供需双方协商确定。 注：1.当供需双方协定要求提供室温力学性能时，其力学性能应按本表规定。 2.ZG30Cr7Si2、ZG40Cr13Si2、ZG40Cr17Si2、ZG40Cr24Si2、ZG40Cr28Si2、ZGCr29Si2可以在800～850℃进行退火处理。若需要，ZG30Cr7Si2也可在铸态下供货。其他牌号耐热钢和合金铸件，不需要热处理。若需热处理，则热处理工艺由供需双方商定，并在订货合同中注明。 3.本表列出的最高使用温度为参考数据，这些数据仅适用于牌号间的比较，在实际应用时，还应考虑环境、载荷等实际使用条件。 |
|||||