板材室温力学性能(GB/T 3621—2007) |
||||||
|
牌号 |
状态 |
板材厚度 /mm |
抗拉强度 Rm/MPa |
规定非比例延伸强度 Rp0.2/MPa |
断后伸长率① A/%，不小于 |
|
|
TA1 |
M |
0.3~25.0 |
≥240 |
140~310 |
30 |
|
|
TA2 |
M |
0.3~25.0 |
≥400 |
275~450 |
25 |
|
|
TA3 |
M |
0.3~25.0 |
≥500 |
380~550 |
20 |
|
|
TA4 |
M |
0.3~25.0 |
≥580 |
485~655 |
20 |
|
|
TA5 |
M |
0.5~1.0 ＞1.0~2.0 ＞2.0~5.0 ＞5.0~10.0 |
≥685 |
≥585 |
20 15 12 12 |
|
|
TA6 |
M |
0.8~1.5 ＞1.5~2.0 ＞2.0~5.0 ＞5.0~10.0 |
≥685 |
— |
20 15 12 12 |
|
|
TA7 |
M |
0.8~1.5 ＞1.6~2.0 ＞2.0~5.0 ＞5.0~10.0 |
735~930 |
≥685 |
20 15 12 12 |
|
|
TA8 |
M |
0.8~10 |
≥400 |
275~450 |
20 |
|
|
TA8-1 |
M |
0.8~10 |
≥240 |
140~310 |
24 |
|
|
TA9 |
M |
0.8~10 |
≥400 |
275~450 |
20 |
|
|
TA9-1 |
M |
0.8~10 |
≥240 |
140~310 |
24 |
|
|
TA10② |
A类 |
M |
0.8~10.0 |
≥485 |
≥345 |
18 |
|
B类 |
M |
0.8~10.0 |
≥345 |
≥275 |
25 |
|
|
TA11 |
M |
5.0~12.0 |
≥895 |
≥825 |
10 |
|
|
TA13 |
M |
0.5~2.0 |
540~770 |
460~570 |
18 |
|
|
TA15 |
M |
0.8~1.8 ＞1.8~4.0 ＞4.0~10.0 |
930~1130 |
≥855 |
12 10 8 |
|
|
TA17 |
M |
0.5~1.0 ＞1.1~2.0 ＞2.1~4.0 ＞4.1~10.0 |
685~835 |
— |
25 15 12 10 |
|
|
TA18 |
M |
0.5~2.0 ＞2.0~4.0 ＞4.0~10.0 |
590~735 |
— |
25 20 15 |
|
|
TB2 |
ST STA |
1.0~3.5 |
≤980 1320 |
— |
20 8 |
|
|
TB5 |
ST |
0.8~1.75 ＞1.75~3.18 |
705~945 |
690~835 |
12 10 |
|
|
TB6 |
ST |
1.0~5.0 |
≥1000 |
— |
6 |
|
|
TB8 |
ST |
0.3~0.6 ＞0.6~2.5 |
825~1000 |
795~965 |
6 8 |
|
|
TC1 |
M |
0.5~1.0 ＞1.0~2.0 ＞2.0~5.0 ＞5.0~10.0 |
590~735 |
— |
25 25 20 20 |
|
|
TC2 |
M |
0.5~1.0 ＞1.0~2.0 ＞2.0~5.0 ＞5.0~10.0 |
≥685 |
— |
25 15 12 12 |
|
|
TC3 |
M |
0.8~2.0 ＞2.0~5.0 ＞5.0~10.0 |
≥880 |
|
12 10 10 |
|
|
TC4 |
M |
0.8~2.0 ＞2.0~5.0 ＞5.0~10.0 10.0~25.0 |
≥895 |
≥830 |
12 10 10 8 |
|
|
TC4ELI |
M |
0.8~25.0 |
≥860 |
≥795 |
10 |
|
|
① 厚度不大于0.64 mm的板材，延伸率报实测值。 ② 正常供货按A类，B类适应于复合板复材，当需方要求并在合同中注明时，按B类供货。 |
||||||