最小有效渗氮层深度、最低表面硬度与试验力之间的关系(JB/T 8555—1997) |
|||||||
|
最小有效渗 氮层深度 /mm |
最 低 表 面 硬 度 HV |
||||||
|
200～300 |
＞300～400 |
＞400～500 |
＞500～600 |
＞600～700 |
＞700～800 |
＞800 |
|
|
0.05 |
— |
— |
— |
HV0.5 |
HV0.5 |
HV0.5 |
HV0.5 |
|
0.07 |
— |
HV0.5 |
HV0.5 |
HV0.5 |
HV0.5 |
HV1 |
HV1 |
|
0.08 |
HV0.5 |
HV0.5 |
HV0.5 |
HV0.5 |
HV1 |
HV1 |
HV1 |
|
0.09 |
HV0.5 |
HV0.5 |
HV0.5 |
HV1 |
HV1 |
HV1 |
HV1 |
|
0.1 |
HV0.5 |
HV1 |
HV1 |
HV1 |
HV1 |
HV1 |
HV3 |
|
0.15 |
HV1 |
HV1 |
HV3 |
HV3 |
HV3 |
HV3 |
HV5 |
|
0.2 |
HV3 |
HV3 |
HV5 |
HV5 |
HV5 |
HV5 |
HV5 |
|
0.25 |
HV3 |
HV5 |
HV5 |
HV5 |
HV10 |
HV10 |
HV10 |
|
0.3 |
HV5 |
HV5 |
HV10 |
HV10 |
HV10 |
HV10 |
HV10 |
|
0.4 |
HV5 |
HV10 |
HV10 |
HV10 |
HV10 |
HV30 |
HV30 |
|
0.45 |
HV10 |
HV10 |
HV10 |
HV10 |
HV30 |
HV30 |
HV30 |
|
0.5 |
HV10 |
HV10 |
HV10 |
HV30 |
HV30 |
HV30 |
HV30 |
|
0.55 |
HV10 |
HV10 |
HV30 |
HV30 |
HV30 |
HV50 |
HV50 |
|
0.6 |
HV10 |
HV10 |
HV30 |
HV30 |
HV50 |
HV50 |
HV50 |
|
0.65 |
HV10 |
HV30 |
HV30 |
HV50 |
HV50 |
HV50 |
HV50 |
|
0.7 |
HV10 |
HV30 |
HV50 |
HV50 |
HV50 |
HV50 |
HV50 |
|
0.75 |
HV20 |
HV30 |
HV50 |
HV50 |
HV50 |
HV100 |
HV100 |
|
注：表内检验方法通常是指允许采用最大试验力，允许用较低的试验力代替表中规定的试验力，如用 HV10代替 HV30。 |
|||||||